Effect of Sm(3+)and Mn2+ incorporation on the structure and luminescence characteristics of Zn2SiO4 phosphor
Yükleniyor...
Tarih
2021
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Pergamon-Elsevier Science Ltd
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
To evaluate the dopant effect precisely, X-ray diffraction (XRD) for structural, scanning electron microscopy (SEM) with energy dispersive x-ray spectroscopy (EDS) analysis for morphological, photoluminescence (PL) and thermoluminescence (TL) characteristics of un-doped, 2.0 mol% Sm3+ doped and 2.0 mol% Sm3+;x mol% Mn2+ (x = 0.5, 1.0, 2.0, 4.0) doped Zn2SiO4 phosphors were tested. PL mechanisms of excitation and emission were discussed together with data on the structure and morphology of the samples. The beta doses from 0.1 to 500 Gy with various steps were applied to observe the glow curve readouts after 200 degrees C preheat at a linear heating rate of 2 degrees C/s from RT to 500 degrees C. Zn2SiO4:2.0%Sm3+;0.5%Mn2+ was chosen for further analysis due to having both the most PL and TL peak area. Various heating rate method was used to determine the kinetic parameters as well as initial rise with T-M-T-stop analysis and computerized glow curve deconvolution methods.
Açıklama
Anahtar Kelimeler
Zn2SiO4, Double doping, TL, CGCD, Thermal quenching