Cathodoluminescence and photoluminescence properties of Dy doped La2CaB10O19 phosphor
Yükleniyor...
Tarih
2020
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Elsevier
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
In this study, we report a detailed analysis of the photoluminescence (PL) and cathodoluminescence (CL) properties of La2CaB10O19 (LCB) doped with Dy ion. Dy doped LCB materials were successfully synthesized using a sol-gel combustion method. Dy doped LCB has the monoclinic structure with lattice parameters a = 11.02067 angstrom, b = 6.55755 angstrom, c = 9.10541 angstrom and alpha = gamma = 90.00, and 13 = 91.49?. Under the excitation by a low voltage electron beam and pulse laser at 349 nm, the LCB:Dy3+ phosphor produces the characteristic emission bands of Dy3+ due to intra-configuration transitions of F-4(9/2) -> H-6(15/2) (480 nm, blue), F-4(9/2) -> H-6(13/2) (574 nm, yellow), F-4(9/2) -> H-6(11/2) (662 nm, red) and F-4(9/2) -> H-6(9/2) (752 nm, red). The concentration quenching phenomenon was observed in both CL and PL measurements and optimum doping concentration was estimated to be 2%. We suggest that the concentration quenching mechanism of intense yellow emission at 574 nm was attributed to dipole-dipole interaction for both CL and PL.
Açıklama
Anahtar Kelimeler
La2CaB10O19, Cathodoluminescence, Photoluminescence, Concentration quenching, Dipole-dipole interaction, Spectroscopic Properties, Luminescence, Growth, Lanthanum, Emission, Eu