Integrating K plus into Eu and Tb doped GdCa 4O(BO3)3: A dual study on photoluminescence and structure
Küçük Resim Yok
Tarih
2024
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Elsevier Science Sa
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
In this study, we investigate the structural and photoluminescence (PL) properties of rare -earth -doped GdCa 4 O (BO 3 ) 3 (GdCOB) phosphors, specifically focusing on the spectral behaviour induced by doping with Eu 3 + and Tb 3 + ions. The powder X-ray diffraction (XRD) spectra confirm the formation of a monoclinic phase. The XRD data were also refined by a Rietveld refinement method. The existence of B, O, Ca, Gd, Tb, Eu and K elements was verified by EDS spectra. We introduce a detailed examination of the charge compensation process using Kro ger- Vink notation to clarify the mechanisms essential for tailoring the optical properties of the phosphors. The PL excitation spectrum of GdCOB:Eu 3 + , monitored at 611 nm, reveals sharp excitation peaks at 319, 361, 380, and 392 nm, corresponding to 7 F 0 -> 5 H 3 , 7 F 0 -> 5 D 4 , 7 F 0 -> 7 F 0 , and 7 F 0 -> 5 L 6 transitions, respectively. The PL spectrum under excitation of 392 nm exhibits that phosphors doped with Eu 3 + a significant red emission at 611 nm, which is attributed to the 5 D 0 -> 7 F 2 transition. This emission intensity is particularly enhanced at non-centrosymmetric sites of the Eu 3 + ions. Similarly, the PL excitation spectrum of GdCOB:Tb 3 + , monitored at 552 nm, displays distinct excitation peaks at 316, 341, 353, and 379 nm, which correspond to the transitions 7 F 6 -> 5 D 0, 7 F 6 -> 5 L 7, 7 F 6 -> 5 D 2, and 7 F 6 -> 5 D 3, respectively. Tb 3 +-doped phosphors display a bright green emission, with a dominant peak at 552 nm, resulting from the 5 D 4 -> 7 F 5 transition. Additionally, the introduction of K + ions as co-dopants results in modifications to the local environments of Eu 3 + and Tb 3 + ions. These changes allow for fine-tuning of the emission peaks, significantly enhancing the luminescent output of the phosphors. Optimal doping concentrations of 5 mol% for Eu 3 + and 1 mol% for Tb 3 + enhance luminescent intensity and prevent concentration quenching. This phenomenon, often resulting in reduced PL intensity at higher dopant levels, is primarily due to dipole -dipole interactions, consistent with Dexter's theory of energy transfer. Strategic modulation of doping concentrations, coupled with a deep understanding of energy transfer mechanisms are critical for the development of advanced luminescent materials Our analysis of the Commission de l ' Eclairage (CIE) chromaticity coordinates reveals enhanced energy transfer dynamics in rare -earth -doped borates, facilitating the tuning of luminescent properties. These results not only deepen our understanding of the fundamental physics governing such phosphors but also open pathways for the development of optoelectronic applications requiring consistent color output, such as LED technologies and solid-state lighting.
Açıklama
Anahtar Kelimeler
Photoluminescence, GdCa4O(BO3)3 Phosphors, Eu3+andTb3+Doping, Concentration Quenching, Energy Transfer