Phase transition and luminescence characteristics of dysprosium doped strontium stannate phosphor synthesized using hydrothermal method
Yükleniyor...
Dosyalar
Tarih
2023
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Elsevier Sci Ltd
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
A series of strontium stannate (SrSnO3) doped with Dy3+ ions at various wt % concentrations (1, 2, 3 and 5) were synthesized via hydrothermal reaction and analysed using X-ray diffraction (XRD), energy dispersive spectros-copy (EDS), environmental electron scanning microscope (ESEM), photoluminescence (PL) and, cath-odoluminescence (CL). The XRD results confirmed that all samples were assigned to cubic perovskite-type SrSnO3 structured with the Pm3m space group. The PL emission spectrum of Dy3+ activated samples consisted of some characteristic peaks located at 481 nm, 572 nm, 660 nm and 753 nm, corresponding to (4F9/2 -> 6H15/2, blue), (4F9/2 -> 6H13/2, yellow), 660 nm (4F9/2 -> 6H11/2, red) and 753 nm (4F9/2 -> 6H9/2, red) transitions. The PL emission line intensity is gradually enhanced with an increase in doping concentration up to 3 wt %, followed by concentration quenching. The confinement effects of localized resonant energy transfer might cause higher concentration quenching. PL emission spectra were affected by the temperature range from 10 K to 300 K. PL emission anomalies at 270 K in SrSnO3:Dy3+ have been reported to be consistent with a structural phase tran-sition at this temperature. This work confirms Singh et al.'s observation, revealing that SrSnO3 has a phase transition at 270 K.
Açıklama
Anahtar Kelimeler
Concentration Quenching; Dy Ions; Hydrothermal Reaction; Phase Transition; Resonant Energy Transfer; Strontium Stannate